ASTM E384-11e1

Standard Test Method for Knoop and Vickers Hardness of Materials

中文名稱：

ASTM E384-11e1 《材料努氏硬度和維氏硬度標(biāo)準(zhǔn)試驗(yàn)方法》

代號說明：

This standard is issued under the fixed designation E384; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscript epsilon (ε) indicates an editorial change since the last revision or reapproval.

This standard has been approved for use by agencies of the Department of Defense.

ε1 NOTE—Sections 8.3 and A1.1.4 were editorially corrected in March 2012.

版本說明：

1 This test method is under the jurisdiction of ASTM Committee E04 on

Metallography and is the direct responsibility of Subcommittee E04.05 on Microindentation

Hardness Testing.With this revision the test method was expanded to

include the requirements previously defined in E28.92, Standard Test Method for

Vickers Hardness Testing of Metallic Material that was under the jurisdiction of

E28.06

Current edition approved Aug. 1, 2011. Published August 2011. Originally

approved in 1969. Last previous edition approved in 2010 as E384 – 10e2. DOI:

10.1520/E0384-11E01.

2 For referenced ASTM standards, visit the ASTM website, www.astm.org, or

contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM

Standards volume information, refer to the standard’s Document Summary page on

the ASTM website.

3 Withdrawn. The last approved version of this historical standard is referenced

on www.astm.org.

標(biāo)準(zhǔn)正文

1. Scope

1.1 This test method covers determination of the Knoop and

Vickers hardness of materials, the verification of Knoop and

Vickers hardness testing machines, and the calibration of

standardized Knoop and Vickers test blocks.

1.2 This test method covers Knoop and Vickers hardness

tests made utilizing test forces in micro (9.807 3 10-3 to 9.807

N ) ( 1 to 1000 gf ) and macro (>9.807 to 1176.80 N) ( >1kg

to 120 kgf ) ranges.

NOTE 1—Previous versions of this standard limited test forces to 9.807

N (1 kgf).

1.3 This test method includes all of the requirements to

perform macro Vickers hardness tests as previously defined in

Test Method E92, Standard Test Method for Vickers Hardness

Testing.

1.4 This test method includes an analysis of the possible

sources of errors that can occur during Knoop and Vickers

testing and how these factors affect the accuracy, repeatability,

and reproducibility of test results.

NOTE 2—While Committee E04 is primarily concerned with metals, the

test procedures described are applicable to other materials.

1.5 Units—When Knoop and Vickers hardness tests were

developed, the force levels were specified in units of gramsforce

(gf) and kilograms-force (kgf). This standard specifies

the units of force and length in the International System of

Units (SI); that is, force in Newtons (N) and length in mm or

μm. However, because of the historical precedent and continued

common usage, force values in gf and kgf units are

provided for information and much of the discussion in this

standard as well as the method of reporting the test results

refers to these units.

1.6 This standard does not purport to address all of the

safety concerns, if any, associated with its use. It is the

responsibility of the user of this standard to establish appropriate

safety and health practices and determine the applicability

of regulatory limitations prior to use.

2. Referenced Documents

2.1 ASTM Standards:

C1326 Test Method for Knoop Indentation Hardness of

Advanced Ceramics

C1327 Test Method for Vickers Indentation Hardness of

Advanced Ceramics

E3 Guide for Preparation of Metallographic Specimens

E7 Terminology Relating to Metallography

E29 Practice for Using Significant Digits in Test Data to

Determine Conformance with Specifications

E74 Practice of Calibration of Force-Measuring Instruments

for Verifying the Force Indication of Testing Machines

E92 Test Method for Vickers Hardness of Metallic Materials

E122 Practice for Calculating Sample Size to Estimate,

With Specified Precision, the Average for a Characteristic

of a Lot or Process

E140 Hardness Conversion Tables for Metals Relationship

Among Brinell Hardness, Vickers Hardness, Rockwell

Hardness, Superficial Hardness, Knoop Hardness, and

Scleroscope Hardness

E175 Terminology of Microscopy

E177 Practice for Use of the Terms Precision and Bias in

ASTM Test Methods

E691 Practice for Conducting an Interlaboratory Study to

Determine the Precision of a Test Method

E766 Practice for Calibrating the Magnification of a Scanning

Electron Microscope

2.2 ISO Standards:

ISO 6507-1 Metallic Materials—Vickers hardness Test—

Part 1: Test Method

ISO/IEC 17011 Conformity Assessment—General Requirements

for Accreditation Bodies Accrediting Conformity

Assessment Bodies.

ISO/IEC 17025 General Requirements for the Competence

of Testing and Calibration Laboratories