International Standard  ISO 6508-1:2015(E) 

Metallic materials — Rockwell hardness test — 

Part 1: 

Test method

ISO 6508 consists of the following parts under the general title Metallic materials —— Rockwell hardness test:

ISO 6508-1 Metallic materials —— Rockwell hardness test Part 1: Test method

ISO 6508-2 Metallic materials —— Rockwell hardness test Part 2: Verification and calibration of testing machines and indenters

ISO 6508-3 Metallic materials —— Rockwell hardness test Part 3: Calibration of refernce blocks

Content

Foreword 
1 Scope
2 Normative references
3 Principle
4 Symbols, abbreviated terms and designations
5 Testing machine
6 Test piece
7 Procedure
8 Uncertainty of the results
9 Test report
10 Conversions to other hardness scales or tensile strength values
Annex A (normative) Special HR30TSm and HR15TSm test for thin products
Annex B (normative) Minimum thickness of the test piece in relation to the Rockwell hardness
Annex C (normative) Corrections to be added to Rockwell hardness values obtained on 

            convex cylindrical surfaces
Annex D (normative) Corrections to be added to Rockwell hardness C scale values obtained 

            on spherical test surfaces of various diameters
Annex E (normative) Daily Verification Procedure
Annex F (normative) Inspection of diamond indenters
Annex G (informative) Uncertainty of the measured hardness values
Annex H (informative) CCM - Working Group on Hardness
Annex I (informative) Rockwell Hardness Measurement Traceability
Bibliography


1  Scope

This part of ISO 6508 specifies the method for Rockwell regular and Rockwell superficial hardness tests
(scales and applicable range of application according to Table 1) for metallic materials and is applicable
to stationary and portable hardness testing machines.

For specific materials and/or products, other specific International Standards apply (for instance,

ISO 3738-1 and ISO 4498).

NOTE Attention is drawn to the fact that the use of tungsten carbide composite for ball indenters is 

considered to be the standard type of Rockwell indenter ball. Steel indenter balls are allowed to continue

to be used only when complying with Annex A.


2  Normative references

The following documents, in whole or in part, are normatively referenced in this document and are
indispensable for its application. For dated references, only the edition cited applies. For undated
references, the latest edition of the referenced document (including any amendments) applies.

ISO 6508-2:2015，Metallic materials — Rockwell hardness test — Part 2: Verification and calibration of
testing machines
ISO 6508-3:2015，Metallic materials — Rockwell hardness test — Part 3: Calibration of reference blocks

相關(guān)標(biāo)準(zhǔn)

國(guó)家標(biāo)準(zhǔn)GB/T 230.1-2018《金屬材料 洛氏硬度試驗(yàn) 第1部分：試驗(yàn)方法》

       本標(biāo)準(zhǔn)修改采用國(guó)際標(biāo)準(zhǔn)ISO6508-1:2005《金屬材料 洛氏硬度試驗(yàn) 第1部分:試驗(yàn)方法(A、B、C、D、E、F、G、H、K、N、T 標(biāo)尺)》(英文版)。 

       本標(biāo)準(zhǔn)根據(jù)ISO6508-1:2005重新起草,根據(jù)我國(guó)的實(shí)際情況,本標(biāo)準(zhǔn)在采用國(guó)際標(biāo)準(zhǔn)時(shí)進(jìn)行了修改和補(bǔ)充。這些技術(shù)性差異用垂直單線標(biāo)識(shí)在它們所涉及的條款的頁(yè)邊空白處。 

       本標(biāo)準(zhǔn)結(jié)構(gòu)和技術(shù)內(nèi)容與ISO6508-1:2005基本一致,根據(jù)我國(guó)情況在以下幾方面進(jìn)行了修改: 

       —— 刪去了國(guó)際標(biāo)準(zhǔn)的前言; 

       —— 刪除了引言; 

       —— 本國(guó)際標(biāo)準(zhǔn)一詞改為本標(biāo)準(zhǔn); 

       —— 用小數(shù)點(diǎn).代替作為小數(shù)點(diǎn)的,; 

       —— 增加了對(duì)試樣表面粗糙度的建議; 

       —— 增加了試驗(yàn)結(jié)果有效位數(shù)的規(guī)定; 

       —— 修改了附錄G 洛氏硬度測(cè)量值的不確定度分析方法。